TOP > Anticorrosive agents > Anticorrosive agents

CP-CU

 
Very effective anticorrosion and prevent discoloration of copper and copper alloy
Low viscosity (lower than 4 ㎟/s), ultra thin soft oil based film (1 - 2 µm), not sticky
Stable non reactive compound, harmless to people, no irritative odour
Easily degrease by hydrocarbon solvent
About 3 months of anticorrosive term

CP-4000LA


 
    
No irritative odour
Reasonably low viscous oil based anticorrosive agent
Generate soft film (2 - 5 µm) after applied
Enable to remove the film by any degreasing agents
More than 1 year of anticorrosive term when used indoor (varies with surrounding condition)
Excellent oil stain resistant effect

CP-4000


Oil based anticorrosive agent This agent developed particularly for export purpose!!
    
Most suitable anticorrosive agent for under long term adverse conditions such as export acrossing equator
Excellent moisture displacing properties
Cost effective, enable to treat large area with small amount (more than 60 ㎡/L)
Generate reasonably thick soft film (2 - 5 µm) after applied.
Easily degrease the film by any degreasing agents
The film remain soft
Enable to operate without degrease the film

CP-3


Protect all kinds of metal surfaces from rusting and corrosion!!
        
    
Excellent moisture displacing properties, eliminate moist on metal surface and keep preventing from it
Low viscosity (less than 3 ㎟/s), generate extremely thin soft imperceptible oil based film (2 - 3µm) and tackiness disappeared within 10 - 15 minutes after applied
1 - 2 years of anticorrosive term without oil stain, suited for long term indoor anticorrosion of ferrous metal
Cost effective, enable to treat large area with small amount (about 150 - 200 m²/L)
Less affect on resin and easily degreased
Harmless to people, almost odourless, stable non reactive compound

Mecha-hibitor #60


 
    
Excellent water soluble anticorrosive agent
Economically friendly due to its high dilution factor.
Non flammable and perform as effective anticorrosion as oil based agent.
Generate no tackiness ultra thin film (less than 1μm) as it dried, and easily remove the film by alkaline detergent.
It is suitable anticorrosion for ferrous metal after cut/grinded by using water soluble lubricant.

Mecha-hibitor # 31


 
    
Possible to use in dilution with water, economical high dilution ratio (20 - 50 time)
Easily spread and non-sticking solution on metal surface
Easily removed by water
Contain no harmful compounds such as sodium nitrite, chromic acid, therefore safe to people
About 15 - 30 days of anticorrosive term when used at indoor atmosphere

Metal All IH-A

Effective anticorrosion and prevent discolouration for iron, copper alloys (copper, brass, phosphor bronze), aluminium alloy and cemented carbide
Economical high dilution ratio (20 - 60 times)
Easily spread and non-sticking solution on metal surface
Easily removed by water
Contain no harmful compounds such as sodium nitrite, chromic acid, therefore safe to people